Search found 3093 matches
- by cj737
- Wed Jan 03, 2024 9:01 am
- Forum: Welding Forum General Shop Talk
- Topic: Argon Cylinder Trade In Math
- Replies: 4
- Views: 3187
Re: Argon Cylinder Trade In Math
I don’t see how having a single larger bottle will solve your setup problems. Can you be more specific about what the actual problem is?
- by cj737
- Mon Jan 01, 2024 3:11 pm
- Forum: Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- Topic: TIG welding pipe using stick electrode as filler
- Replies: 4
- Views: 4002
Re: TIG welding pipe using stick electrode as filler
You should read the comments on that video. Typically people will use the proper TIG rod that already has a flux coating, use a flux paste, or simply use SMAW process if you’re using SMAW rods. It’s a hack that doesn’t make much sense to me. And it would never pass code work in sanitary pipe.
- by cj737
- Mon Jan 01, 2024 10:28 am
- Forum: Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- Topic: Furick ALLY#5 for #17 torch
- Replies: 2
- Views: 1745
Re: Furick ALLY#5 for #17 torch
The #5 can also use a wedge collet, but that does not look like a Furick cup. Similar, but not the same.
- by cj737
- Sat Dec 30, 2023 5:17 pm
- Forum: Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- Topic: trouble with oxidization welding stainless
- Replies: 53
- Views: 27665
Re: trouble with oxidization welding stainless
I find it odd that you, as a new welder have such determination to ignore sound advice, and would speak so poorly of someone (Pacific Arc Tig) who has been welding for 20 years in a production environment. He clearly shows smaller cups in that video, but you seem to know everything yet can’t produce...
- by cj737
- Fri Dec 29, 2023 11:53 pm
- Forum: Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- Topic: trouble with oxidization welding stainless
- Replies: 53
- Views: 27665
Re: trouble with oxidization welding stainless
All of the examples in your latest picture show issues.
Maybe this video will help https://youtu.be/PE59reAtJRs?si=dn20UqUdyX0_zc60
Maybe this video will help https://youtu.be/PE59reAtJRs?si=dn20UqUdyX0_zc60
- by cj737
- Thu Dec 28, 2023 11:50 pm
- Forum: Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- Topic: 3/8" Stainless Fillet Settings
- Replies: 10
- Views: 5961
Re: 3/8" Stainless Fillet Settings
If you weld the plates down, then you don’t have to allow much cooling between stitches. But let it cool fully before cutting the tacks loose.
- by cj737
- Thu Dec 28, 2023 10:05 am
- Forum: Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- Topic: trouble with oxidization welding stainless
- Replies: 53
- Views: 27665
Re: trouble with oxidization welding stainless
It’s STILL a matter of gas coverage and cup size. You seem unwilling to use the recommended sizes and flow, so oxidation/overheating will occur no matter how fast you travel, what size filler, and how amps you use.
Until you change those variables, nothing will improve.
Until you change those variables, nothing will improve.
- by cj737
- Thu Dec 28, 2023 12:04 am
- Forum: Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- Topic: 3/8" Stainless Fillet Settings
- Replies: 10
- Views: 5961
Re: 3/8" Stainless Fillet Settings
I too would weld in “quadrants” but I’d start in the middle with tacks, then out to the ends, tack, alternating sides and moving around. Think about the weld you just put down, where will it pull against? Weld there next to balance the stress. 180 amps seems high to me, I’d be lower and when stitchi...
- by cj737
- Mon Dec 18, 2023 10:48 am
- Forum: Welding Forum General Shop Talk
- Topic: generator vs welder generator
- Replies: 2
- Views: 2065
Re: generator vs welder generator
One machine versus two. Welders that have built-in generators also usually produce far more available power than “portable generators”. You also have differing types of current generation within the generator market. So, not all generators can power a welder due to power draw.
- by cj737
- Thu Dec 14, 2023 11:05 pm
- Forum: Metal Cutting
- Topic: Why are oxyacetylene cutting preferred over plasma?
- Replies: 8
- Views: 7695
Re: Why are oxyacetylene cutting preferred over plasma?
Then I guess you know everything without the need to pose a question.
- by cj737
- Thu Dec 14, 2023 5:04 pm
- Forum: Metal Cutting
- Topic: Why are oxyacetylene cutting preferred over plasma?
- Replies: 8
- Views: 7695
Re: Why are oxyacetylene cutting preferred over plasma?
Plasma cutters are limited in amperage to the total thickness they can cut. It requires a lot of amps to rip through 2” thick stock. Whereas an OA setup really only needs an appropriate tip to deal with very thick material. As for shops that only have OA, perhaps they only deal with mild steel and i...
- by cj737
- Wed Dec 13, 2023 7:42 pm
- Forum: Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- Topic: Big gush of argon?
- Replies: 27
- Views: 12294
Re: Big gush of argon?
This entire years old thread is a solution in search of a problem. :roll: A single, moment of a rush of argon is completely inconsequential to welding. Anyone who doesn’t tap a pedal when first setting up, or checking for leaks after a tank swap is an alien. You can’t even begin to calculate the “lo...
- by cj737
- Wed Dec 13, 2023 9:21 am
- Forum: Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- Topic: Glass cups
- Replies: 8
- Views: 14166
Re: Glass cups
I've seen those Chinese green o ring gas lenses and glass cup, what's your experience with them? Is the furrick cup much better? It's like 20 times the price. The Chinese standard cup works well so far. The Furick cups also are designed to be used with a specially manufactured gas lens that has an ...
- by cj737
- Sun Dec 03, 2023 11:32 pm
- Forum: Member Introductions
- Topic: is this fixable?
- Replies: 2
- Views: 19735
Re: is this fixable?
I doubt heavily that a welder with a certification at risk would weld that. There’s too much liability in doing it. Same thing with climbing stands for deer hunters.
- by cj737
- Fri Nov 17, 2023 11:32 pm
- Forum: Stick Welding/Arc Welding - Shielded Metal Arc Welding
- Topic: My vertical up really needs help
- Replies: 6
- Views: 17055
Re: My vertical up really needs help
I run about the same DIG and the amps are pretty close (every machine, every person welds just a bit differently). It looks better, but your covering beads still look narrow on the manipulation to me. The root pass looks a bit slow in travel, but the tie-ins look way better to me. Remember, vertical...
- by cj737
- Fri Nov 17, 2023 5:15 pm
- Forum: Stick Welding/Arc Welding - Shielded Metal Arc Welding
- Topic: My vertical up really needs help
- Replies: 6
- Views: 17055
Re: My vertical up really needs help
Travel speed looks off to me. And I’d try to move a bit side-to-side to tie in the toes better ( makes a wider, less ropey bead). Your amps seem a bit high too. Try lowering to 95 and use some movement and see if a lower heat and wider travel don’t help you get what you want. You can always bump up ...
- by cj737
- Tue Nov 14, 2023 8:58 am
- Forum: Mig and Flux Core - gas metal arc welding & flux cored arc welding
- Topic: 100% argon for mig welding
- Replies: 7
- Views: 23008
Re: 100% argon for mig welding
You could use 100% Argon to MIG but would have to switch to Silicon Bronze filler wire. Else, not a good choice.
- by cj737
- Mon Oct 30, 2023 9:54 pm
- Forum: Member Introductions
- Topic: New to the Forum
- Replies: 3
- Views: 16997
Re: New to the Forum
Make sure you purge those stainless welds! You can buy, make or cobble together some inexpensive purging kits.
- by cj737
- Mon Oct 30, 2023 6:36 am
- Forum: Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- Topic: Help: want to add 2nd solenoid valve for back purge line
- Replies: 14
- Views: 22805
Re: Help: want to add 2nd solenoid valve for back purge line
One thing I'd try first is to use a larger cup and some higher CFH. That material looks pretty "shagged out" to begin with, so some amount of discoloration is inevitable. Have you considered using Silicon Bronze wire? That looks to be a rust repair patch panel. I have great success with Si...
- by cj737
- Sun Oct 29, 2023 8:16 pm
- Forum: Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- Topic: Help: want to add 2nd solenoid valve for back purge line
- Replies: 14
- Views: 22805
Re: Help: want to add 2nd solenoid valve for back purge line
I’ve never purged mild steel. I’ve also not encountered “scale” on the backside of a weld to be an issue, stainless, CroMo, Ti, you bet I’d purge those. Are you cleaning the material properly on both sides? Are you running too much heat? I’m just asking because I don’t understand the circumstances n...
- by cj737
- Fri Oct 27, 2023 9:48 pm
- Forum: Mig and Flux Core - gas metal arc welding & flux cored arc welding
- Topic: Pulse MIG / Pulse Spray Settings
- Replies: 2
- Views: 5884
Re: Pulse MIG / Pulse Spray Settings
Spray MIG requires both the correct gas mixture and voltage. Pulse settings are heavily dependent on material thickness and wire diameter. It would be very helpful if you provided some basic information so that others can offer input.
- by cj737
- Wed Oct 18, 2023 4:25 pm
- Forum: Mig and Flux Core - gas metal arc welding & flux cored arc welding
- Topic: Mig welding Tip or Trick needed
- Replies: 4
- Views: 6172
Re: Mig welding Tip or Trick needed
I’d probably opt for lower settings and slower speeds and take my time. If you go with 3.2 you’ll be racing to keep from blowing out the material and potentially get a poor weld as a result. If you can read the puddle, using lower settings shouldn’t cause as much issue. Or you could try higher heat ...
- by cj737
- Tue Oct 10, 2023 9:00 am
- Forum: Stick Welding/Arc Welding - Shielded Metal Arc Welding
- Topic: generators
- Replies: 2
- Views: 8898
Re: generators
The issue is with the generator and not much you can do to it/about it to overcome the current capacity. Not all generators will run welding machines, even when they advertise ample range. I’ve had a similar issue with running a power saw on a generator in the field to cut steel. Damn thing wouldn’t...
- by cj737
- Sun Oct 01, 2023 2:46 pm
- Forum: Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- Topic: Lincoln Square Wave 200 Inverter Tig read out
- Replies: 4
- Views: 6277
Re: Lincoln Square Wave 200 Inverter Tig read out
If it doesn’t have that, then does your amperage vary at the torch with more or less pedal depressed? Set the amperage to 150, then only depress the pedal a small amount. Is the arc strength behaving correctly? I don’t have that machine so I’m asking some routine questions. If the display isn’t chan...
- by cj737
- Sun Oct 01, 2023 1:03 pm
- Forum: Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- Topic: Lincoln Square Wave 200 Inverter Tig read out
- Replies: 4
- Views: 6277
Re: Lincoln Square Wave 200 Inverter Tig read out
Are you setup in 2T or 4T?
Jump to
- Introductions & How to Use the Forum
- ↳ Welcome!
- ↳ Member Introductions
- ↳ How to Use the Forum
- ↳ Moderator Applications
- Welding Discussion
- ↳ Metal Cutting
- ↳ Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- ↳ Mig and Flux Core - gas metal arc welding & flux cored arc welding
- ↳ Stick Welding/Arc Welding - Shielded Metal Arc Welding
- ↳ Welding Forum General Shop Talk
- ↳ Welding Certification - Stick/Arc Welding, Tig Welding, Mig Welding Certification tests - Welding Tests of all kinds
- ↳ Welding Projects - Welding project Ideas - Welding project plans
- ↳ Product Reviews
- ↳ Fuel Gas Heating
- Welding Tips & Tricks
- ↳ Video Discussion
- ↳ Wish List
- Announcements & Feedback
- ↳ Forum News
- ↳ Suggestions, Feedback and Support
- Welding Marketplace
- ↳ Welding Jobs - Industrial Welding Jobs - Pipe Welding Jobs - Tig Welding Jobs
- ↳ Classifieds - Buy, Sell, Trade Used Welding Equipment
- Welding Resources
- ↳ Tradeshows, Seminars and Events
- ↳ The Welding Library
- ↳ Education Opportunities