it help when you make 50 or 100 tack at day on very thin metal were the distance between the electrode​ and the metal are very important for make the tack and not burn the two pieces, with this you make the same tack every time like the first

Inviato dal mio U FEEL utilizzando Tapatalk

hi guys, i make this simple wheel guide looked on the torch cup for make easy and precise tack and welding on thin pipe, work very good on welding without filler rood such as 0,8mm steel (in picture) with 0,4mm gap between electrode and piece https://uploads.tapatalk-cdn.com/20170711/12607ae1004274b...

just an other question before i buy this Torch, can i use it without the water inside at low amperage while i make my homemade cooling unit or can i damage the torch ?

Inviato dal mio U FEEL utilizzando Tapatalk

i weld just simple aluminum stuff from 2-3 mm thickness, and some repair like broken radiator or motorcycle crankchase but the amperage are near 200amp, i think this isn't a problem because i don't weld aluminum for hours... i was looking some torches on ebay , what's the differences between this tw...

thanks for answer my post, i was oriented to buy CK torch but im not sure what style is the most appropriate, i weld a lot of sheet steel but also happens me to weld some aluminum (wp9 style can do this job al 200amp?) and i have a lot of cups for my wp26 torch ( is it compatibles or i have to buy c...

hi guys, after several hours welding exhaust pipes i have notice that my torch(wp26 style air cooled) get very hot, in this pic i have put Jody's tig finger around my torch for finish my work :D , i think to change my torch to a small water cooled so i can save time... what type of torch can i buy c...

trying with standard n°7 cup instead of gas lens, 30% balance ( the lower i can setting) more focused arch lenghts slow my traveling speed and wait for great melting before fill the rod, it seems im going to the right direction, more penetration, i tryed different filling rod; in the photo i used 40...

What machine do you have that has that many wave forms but only 100Hz for frequency options? i think is made is the same place where everlast is made because its very similar, have the same interface,function, maybe have limited frequency because is cheaper hahaha https://uploads.tapatalk-cdn.com/2...

Which side of the T did you weld first? Smart money says the right (in the sectioned photo) where you base metal was not hot enough. By the time you weld one side, the base is now very hot, and the penetration much greater for the other side. Having sufficient heat to melt the filler is not enough ...

Hi guys, today while i was welding 2mm aluminum t-joint i thought to cut it and put some welding cleaner gel (how says jody if you aren't certe of your weld cut it) and see if is a goood weld, so i found no great penetration, luckily it was a test before welding other pieces, whats is wrong? im usin...

some practice with an aluminum box

Here a short video of how it's working made on my garage, non a very professional welding table :mrgreen: , simple regolation of speed by a H0 train transformer with reverse switch, on the floor: on the left there is the foot switch connected whit spindle motor (regulation of the speed with on/of on...

Looks pretty darn nice. Only one question- is it your laser cutter or someone else's? I want to get one someday if I have the money just to say I have one. That seems like it would be fun. Unfortunatly these machines are very expensive, the one who did this job is a professional laser cutter of a f...

this is the second i made, very super low cost spindle made from laser cut steel tig welded, three indipendent jaw for welding light things. The gear reducer is take from an old 12v door opener, very low speed :P https://uploads.tapatalk-cdn.com/20170618/f3d989627f8f83733e870b022e606793.jpg https://...

I never thought it was so difficult to make a good tack, nex time i will buy a welding machine with spot function hahaha

trying with alluminum bar inside the piece but tack penetrete to much, no porosity but very close to have it, so i change my setting to a 33pps, welding current to 70 amp (lower) base current 33% and put a tack, last photo welded with the same settings and without alluminum bar inside. In the first ...

Today i made two simple cordless drill holders and weld four adjustable legs for an assembly table made for line assembly of kitchen ovens. All make with 304 stainless steel scarp from ovens productions, the square tube for the legs are just 1mm thickness tig welded

Any tips for tacking ? unfortunately my welder havent the spot function, so i have to switch as fast as i can the torch button , less welding current forces me to wait much time for tack, and the penetration goes deeper, i try nopulse current but sometimes the tack go bad and melt the two pieces wit...

forgot to say that i'm using n°7 gas len with 2,4 thoriated tungsten , 6lt/min gas flow, piece cleaned with nitro diluent (maybe i can try acetone), here a couples of flat piece i welded above a copper plate, the porosity doesn't appear but i can't weld every time with a copper piece on the back of ...

Hi guys, hope someone can help me, i've to weld some exhaust pipe so i'm training with a pipe made fron sheet bended 0.8mm mild steel, i put three tack on it with this settings, welding current 110Amp, 24pps 33% on Time 20% back current, finding this setting very helpful from a fronius tack video, i...

Hello guys, first of all thank you Jody for all the videos you've done, very helpful for me. About me, as you can read from the title of the post i'm from italy,( sorry form my english) i'm 23 and welding since 18, i learn brazing, oxyacetylen welding and stik welding from my father but tig is my fa...