yea, thanks, that does sound like what im talking about. however what is a creep strength enhanced ferritic steel. Thanks for your previous response. Adam

I am a pipe welder and we never use high frequency. We always use the set up that you have available and it shoots X-ray without any problems. However you won't be able to weld aluminum but sounds like you already know that. Personally I prefer tig welding scratch start and the more you do it the le...

I have also had great success with a #6 and the use of a gas lens. I run my flow at 10-15. If you drop in cup size you will have to reduce your flow even more. I'd say keep it about 7-10. I once was using a #4 cup and didn't reduce my flow (although I was using more gas probably 25-35) I was getting...

Hi there, I am a pipe welder and am wondering if anybody knows the numerical classification of 9 chrome pipe. I am aware of its piping applications and "runny" welding characteristics but nobody can tell me anything about it other than its 9% chrome, and Im not sure thats even accurate. It...