I definetley will stay on the forum, I see you are from oz where are you?

Hi mates!!! I tryied to sandwich those two plates when I was welding it with Tig and really help but still pull a bit, was acceptable any way. Unfortunatley was very slow so at the end I welded it with Mig. Still sandwiched two plates and welded fully both side, and looks very good was quite straigh...

Cracking tack problem is solve thank you all welders!!! But there is another thing I want to ask you. Dont really weld ally ticker than 3mm as Im working for sheet metal shop but this time I have got 6 mm ally checker plate to weld together. Its a butt joint 1500mm (5ft)long each section is 1200mm (...

Thanks WerkSpace I watched the video and it make a sense I had to set up AC balance a bit higher. Good video explain clearly AC balance

Thanks

Many thanx guys for quick respond. TamJeff I have follow your advices and its ok many thanks, 2.4 filler is 2.4 mm (3/32) ally filler 4043 5% silicone. I have more plates to weld tomorrow so will try tacking up with gap instead of beveled it. Im using 3.2 mm (white tip) tungsten and when I turn the ...

Hello welders! I was welding checker ally plate 6 mm tick and during tackink the tack had cracked every one. When I start welding it weld cracked to question is why? Facts: I was useing 2.4 ally filler with 5% silicone welder was setup around 200 amps plate was v grooved on both sides half way, I di...