ofcourse i am concered of being explode, what i am tryig to say is this fuel tank cleand very good more then a month ago ,i left it open outside till now , the tank dont have even a gasoline smell and it is still open in my small work room. this is the reason i am not concered, i wouldnt touch it if...

i already cleaned with soup and water and let it dry for a month opened, i dont worry from explosine, i am worry with making a hole in this tank.

i bought the big tank refill is about 80-90$ here, i am allmost finishing it. i have a sump i want to weld to my fuel tank (i am not going to do it now dont want to mess my tank) and i want to practice on this. the sump is 304ss 3mm and the fuel tank is steel about 1mm, what thung size to use? fille...

made some practice on steel, then welded two parts this is the result

i am wasting too much argon on practice do you think i should weld without it till i get it

thanks!!!

yea this is exacly the problem i am moving the finger not the arm, i am trying to work on this.

i practiced on steel today trying to move only my arm ,will post pictures later.

thanks mike,

ok after some practice on 3mm ss304 this is the result, 2.4mm thun and 1.6 filler.

any advices will be apriciated

Hello, i am new to tig welding and i just got my JLT210 machine. i made beads on 0.7mm SS plate with filler 308 at the begining it looke very bad after adjusting the current it looked clean gold and nice. i tried to weld steel about 2-3mm with 308 filler 1.6mm thung and cup 6 current was 80amp but t...