I just started tig welding aluminum and I cannot figure out what I'm doing wrong. The machine is an ahp alpha tig 200x and the setting I've been using are 150 amps, 3/32 blue tungsten, 25 scfh of argon, 120hz and 35% ac balance. I have just been trying to practice on some 4043 1/8 flat bar. As soon as I light the arc no puddle forms and the whole piece of metal melts. Can someone tell me what I'm doing wrong. I'll attach a picture below. Thanks.
- Attachments
-
- IMG_0106.JPG (38.84 KiB) Viewed 1270 times
Honestly, it looks like you're welding DC.
Also, such small piece will heat saturate quickly so you need to back off the current a lot when it start melting.
Also, such small piece will heat saturate quickly so you need to back off the current a lot when it start melting.
Pictures from my scrap collection:
http://forum.weldingtipsandtricks.com/v ... f=9&t=5677
http://forum.weldingtipsandtricks.com/v ... f=9&t=5677
6061 ? or hardware store special.
Everlast 250EX
Miller 250 syncrowave
Sharp LMV Vertical Mill
Takisawa TSL-800-D Lathe
Coupla Bandsaws,Grinders,surface grinder,tool/cutter grinder
and more stuff than I deserve(Thanks Significant Other)
Miller 250 syncrowave
Sharp LMV Vertical Mill
Takisawa TSL-800-D Lathe
Coupla Bandsaws,Grinders,surface grinder,tool/cutter grinder
and more stuff than I deserve(Thanks Significant Other)
thatoneguy
- thatoneguy
-
Workhorse
-
Posts:
-
Joined:Wed Apr 20, 2016 12:08 pm
-
Location:Texas
I don't think it's a welding on DC issue... I think your amperage might just be way too high... Or you got some crazy weird aluminum... Try taking a stainless brush and scrub the crab out of it, acetone wipe it really well.
Sent from my VS980 4G using Tapatalk
Sent from my VS980 4G using Tapatalk
Everlast Power I-MIG 275P
Everlast Power TIG 250EX
Everlast Power Plasma 80S
Lincoln AC/DC Tombstone
Smith OxyAcetylene
Everlast Power TIG 250EX
Everlast Power Plasma 80S
Lincoln AC/DC Tombstone
Smith OxyAcetylene
Artie F. Emm
- Artie F. Emm
-
Weldmonger
-
Posts:
-
Joined:Thu Jul 24, 2014 7:53 am
25 cfh argon is high, isn't it? i recall reading that too high a flow rate can draw in ambient atmosphere and contaminate the weld. The Miller weld calculator can provide the proper flow rate.
Also, some flow meters are graduated in liters per minute, rather than cubic ft per hour.
Also, some flow meters are graduated in liters per minute, rather than cubic ft per hour.
Dave
aka "RTFM"
aka "RTFM"
- 5th Street Fab
-
Guide
-
Posts:
-
Joined:Sun Jan 15, 2017 1:08 am
Most the guys at my work weld at 25 cfh on aluminum I'm around 15 but it works for them. It'll just be a duller looking weld not as shiny.Artie F. Emm wrote:25 cfh argon is high, isn't it? i recall reading that too high a flow rate can draw in ambient atmosphere and contaminate the weld. The Miller weld calculator can provide the proper flow rate.
Also, some flow meters are graduated in liters per minute, rather than cubic ft per hour.
When you're welding do you hear an annoying buzz? Or does it sound the same as when you're welding steel?
Sent from my SM-G920V using Tapatalk
Most the guys at my work weld at 25 cfh on aluminum I'm around 15 but it works for them. It'll just be a duller looking weld not as shiny.5th Street Fab wrote:Artie F. Emm wrote:25 cfh argon is high, isn't it? i recall reading that too high a flow rate can draw in ambient atmosphere and contaminate the weld. The Miller weld calculator can provide the proper flow rate.
Also, some flow meters are graduated in liters per minute, rather than cubic ft per hour.
When you're welding do you hear an annoying buzz? Or does it sound the same as when you're welding steel?
Sent from my SM-G920V using Tapatalk
I know I'm on ac not dc cause I can change the frequency and it sounds different each time