Well I got it. Have y’all ever had an argon bottle start out dirty and then clean up? Seems like after I tried it again the more I went the cleaner it got. I don’t know. I put my old bottle back on and it was all good so I put the new bottle back on it cleaned up after a while. Crazy.
- Attachments
-
- E08628FC-C4E8-4E04-9ED9-CBEC319AC26C.jpeg (42.09 KiB) Viewed 919 times
- tungstendipper
-
Weldmonger
-
Posts:
-
Joined:Sun Nov 19, 2017 10:09 am
This is what gives us gray hair, and makes our day interesting.
Lincoln MP 210, Lincoln Square Wave 200,
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
- tungstendipper
-
Weldmonger
-
Posts:
-
Joined:Sun Nov 19, 2017 10:09 am
Unfortunately, It's true!jroark wrote:True. Nice user name. Should’ve used that one myself. Haha
Lincoln MP 210, Lincoln Square Wave 200,
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
That makes the two of us. Do you feel like you get consistent results Tig Welding? Especially aluminum? Seems like every job I take I always run into a snag that I have to figure out before I can finish the job. Inexperience? Maybe. I’ve got more in my head than in my hands I guess.
- tungstendipper
-
Weldmonger
-
Posts:
-
Joined:Sun Nov 19, 2017 10:09 am
That why I love to weld aluminum! It makes you fine tune all the little stuff (snags). Consistent results? Haven't tig welded long enough. I am getting better. I'm still wondering what's the big deal about the "stack of dimes" look (tho it's fun to try). A solid weld is more important. This week I'm going to practice on thin metals; stainless and aluminum. Also, outside corners.
All said, I really haven't had to many snags; just my bad eyes not seeing enough. Tri-focals for everyday use, then I had safety glasses made as computer glasses, then added a bi-focal, with a 2.5 cheater lens in my helmet. Now, if I keep my head at the same distance from the arc I can see perfectly!
I only wish I had learned tig welding from the start. It's really the best of all worlds, as long as you don't need speed.
All said, I really haven't had to many snags; just my bad eyes not seeing enough. Tri-focals for everyday use, then I had safety glasses made as computer glasses, then added a bi-focal, with a 2.5 cheater lens in my helmet. Now, if I keep my head at the same distance from the arc I can see perfectly!
I only wish I had learned tig welding from the start. It's really the best of all worlds, as long as you don't need speed.
Lincoln MP 210, Lincoln Square Wave 200,
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
Yeah it’s hard to do a job when you’re on a time crunch. I put my helmet on a 9 shade the other day so I could see the puddle better. It helped but my eyes could tell it. I prefer a 10 or 11 but if I wear safety glasses on a 9 it helps to cut the glare and I can see better.