  • Location:
    New Zealand

was thinking about putting an order in for a big diameter cup gas lens. main use is for stainless.
what do you guys recommend?

at the moment the biggest i have is an 8 which is fine for the thinner stuff (eg 1/16), but i know i have some repairs coming up that will be a lot thicker.
of course i'm a CK fan, but other brands ok as long as they can fit on ck gas lens. for eg the furick cups require their own gas lens.
tweak it until it breaks
cj737
  • Posts:
  • Joined:
    Thu Sep 29, 2016 8:59 am

Fupa 10 or 12 in ceramic. Jody sells them both and they thread straight on. Ceramic because you can walk 'em, the pyrex versions aren't as conducive to it. The Fupa 12 in pyrex with the ring can walk, but it's pricey and you need to use an o-ring to seal it.
Spartan
  • Posts:
  • Joined:
    Fri Mar 06, 2020 8:59 pm

tweake wrote:of course i'm a CK fan, but other brands ok as long as they can fit on ck gas lens. for eg the furick cups require their own gas lens.
I highly recommend Furick. The ceramic versions (and the new version of the glass BBW) will thread onto any CK 2 or 4 series gas lens. No modifications or anything special needed. The glass versions of the 8, 10 and 12 do need a modified gas lens (o-ring groove cut into it) if using the 4 series, but typically can be used on the 2 series gas lenses with no modification.
Weld ON
  • Posts:
  • Joined:
    Tue Mar 09, 2021 5:09 pm

Big caps are used 99% for rage welding and most of time they was made for art welding - ''beauty welding'' , normally not using on torch size 26 ( standard ), normally for micro torch and for sure combination with pedal and fingers glove. You can use your way and try but i will like to ask DO YOU REALLY NEED ...? I have all cups - shape and size . Im just wondering what some of specialist saying on youtube how and for what you have to use :lol: :lol: :lol: . Be honest if you know how to weld and you want to make some next step and you planning to be better as other then go for it.Other way just stay with ceramic and you need size 4 -10 that all most of time 6-7 . Im doing sometimes 1 pack 5KG - 4.0mm a day guess what ... cup 7 -10 ... and on X-ray 96 - 98.8% that most then perfect and without gas lens.

About 1/16 that is 1.57mm most of time you should use cup by need no by thicknes of material . Is to much bad mistic about BIG cups ..:). 101% i can do any job without using glas even i need. This is just my opinion and guys you dont have to agry with anything i writed down .. :)
tweake
  • Posts:
  • Joined:
    Mon Dec 18, 2017 4:53 am
  • Location:
    New Zealand

i mentioned material thickness as an indicator of amps.
just looking at reducing heat tint a bit on the higher amp welds. make cleanup a bit easier.
tweak it until it breaks
Toggatug
  • Posts:
  • Joined:
    Sat Mar 25, 2017 12:06 pm
  • Location:
    Ontario, Canada

Could always go with the monster #24 from arc zone.

If that don't do it set another one up on a trailing arm [emoji14]

Sent from my Pixel 3a using Tapatalk
Poland308
  • Posts:
  • Joined:
    Thu Sep 10, 2015 8:45 pm
  • Location:
    Iowa

I. MAx out on a 12 for certified work. Mostly use an 8
I have more questions than answers

Josh
Spartan
  • Posts:
  • Joined:
    Fri Mar 06, 2020 8:59 pm

Did you get some big cups yet, Tweake? If not, let me know...I'll send you some. BUT figuring out postage to kiwi land is on you ;)
tweake
  • Posts:
  • Joined:
    Mon Dec 18, 2017 4:53 am
  • Location:
    New Zealand

Spartan wrote:Did you get some big cups yet, Tweake? If not, let me know...I'll send you some. BUT figuring out postage to kiwi land is on you ;)
thanks for the offer, but postage is a killer to here. i typically do a big enough order that its worth it. not to mention the time it takes to get here. i have a book on the way at the moment and its almost 2 weeks now. covid is really screwing with shipping.

furick cups i can get here as well as some of the ck stuff.
however the job i was looking at may not end up needing it. looks like its welding 1.6mm to 5mm. i'll know exactly next week.
tweak it until it breaks
cj737
  • Posts:
  • Joined:
    Thu Sep 29, 2016 8:59 am

Tweake - material thickness has little to do with gas coverage (as you know). If its stainless, the #10 or #12 especially, are game changers for weld quality. I prefer the ceramics because the screw on and are more durable.
RonEasley
  • Posts:
  • Joined:
    Mon Feb 01, 2021 5:40 pm
  • Location:
    San Antonio, TX

I have a 26 style torch which I attached a 12 ceramic cup to, I love it.

Learning to "walk the cup" is the challenge.
Ron E

EZ Metal Werx
San Antonio, TX
sbaker56
  • Posts:
  • Joined:
    Sat Feb 08, 2020 12:12 am

I didn't see you mention if your torch was watercooled or air cooled, but regardless I would suggest a Fupa 12 too along with a stubby gas lens kit if you run an air cooled torch. I got a Jazzy 10 and it's noticeably better compared to a equally sized 10 cup, It impressed me enough I'm probably going to post a review about it.

The ceramic cups will fit on any gas lens for a 9/20 torch and any stubby kit for a 17/26, which I would highly highly recommend if you don't already have one.
tweake
  • Posts:
  • Joined:
    Mon Dec 18, 2017 4:53 am
  • Location:
    New Zealand

all ordered.
got a jazzy 10 and fupa 12 on its way, plus other bits.
that should give me plenty of gear for the repairs in the coming weeks.
tweak it until it breaks