Hollywood1
  • Posts:
  • Joined:
    Mon Feb 23, 2015 9:05 am
  • Location:
    Washington

Here is my first attempt at tig welding .078" 5052. I think I welded it too cold. thanks for any advice john.
Attachments
DSCN0782.JPG
DSCN0782.JPG (36.5 KiB) Viewed 1724 times
Top
Rick_H
  • Posts:
  • Joined:
    Sat Feb 08, 2014 1:50 pm
  • Location:
    PA/MD

The RH vertical appears to have a crack about half way up...is that true or just the picture?

What were your settings? 5052 flows real nice, easier to weld IMO? On outside corner joints fit up is everything....
I weld stainless, stainless and more stainless...Food Industry, sanitary process piping, vessels, whatever is needed, I like to make stuff.
ASME IX, AWS 17.1, D1.1
Instagram #RNHFAB
Top
Hollywood1
  • Posts:
  • Joined:
    Mon Feb 23, 2015 9:05 am
  • Location:
    Washington

I just made an extra pass on each vertical leg messing around. No crack. Any recommendations on what you would use for settings for this material thickness. 1/16th tungsten, 1/16 filler. thanks john
Top
User avatar
  • Posts:
  • Joined:
    Thu Dec 26, 2013 12:41 am
  • Location:
    Laredo, Tx

Hollywood1 wrote:I just made an extra pass on each vertical leg messing around. No crack. Any recommendations on what you would use for settings for this material thickness. 1/16th tungsten, 1/16 filler. thanks john
settings on WHATmachine?
Image
Top
Hollywood1
  • Posts:
  • Joined:
    Mon Feb 23, 2015 9:05 am
  • Location:
    Washington

Thermal arc 186
Top
massacre
  • Posts:
  • Joined:
    Sat Feb 28, 2015 10:20 pm
  • Location:
    Massachusetts

Looks pretty good for first attempt IMHO
Top
Hollywood1
  • Posts:
  • Joined:
    Mon Feb 23, 2015 9:05 am
  • Location:
    Washington

Thanks . Aluminum is not easy I've decided.
Top
Hollywood1
  • Posts:
  • Joined:
    Mon Feb 23, 2015 9:05 am
  • Location:
    Washington

Turned up the heat a little bit and was quite a bit easier to tack and welded much nicer! Could be using the wrong setup though-9 torch w. 1/16th tungsten. Here's a couple more pics. Thanks for the advice. John.
Attachments
DSCN0799.JPG
DSCN0799.JPG (30.73 KiB) Viewed 1630 times
Top
Hollywood1
  • Posts:
  • Joined:
    Mon Feb 23, 2015 9:05 am
  • Location:
    Washington

Another picture.
Attachments
DSCN0796.JPG
DSCN0796.JPG (39.81 KiB) Viewed 1630 times
Top
Hollywood1
  • Posts:
  • Joined:
    Mon Feb 23, 2015 9:05 am
  • Location:
    Washington

One more picture using step and pause. Thanks Jody, I'm addicted to tig welding.
Attachments
DSCN0806 (2).JPG
DSCN0806 (2).JPG (61.03 KiB) Viewed 1611 times
Top
dirtmidget33
  • Posts:
  • Joined:
    Tue May 13, 2014 5:22 pm

I have TA 186 I would start off and adjust from following settings

1/16 2% Lathanatied tungsten
7-8 cup with gas lens
85 amps (I use foot pedal)
1 sec pre-flow (I never change this setting on mine)
0 hot start (I don't use setting much, but hammer pedal on aluminum starts.
130-150 AC frequency
10-15% Wave Balance (your metal looks really new so this is where I weld new metal at. You might have to increase as needed. you might be more comfortable at 30) On a side note TA 186 % setting on this is how much it is in cleaning/positive side.
5-7 seconds post flow

Hope this helps. I hardly ever use pulse, use pedal instead. Out of curiosity what where all your settings.
why use standard nozzles after gas lens where invented. Kinda of like starting fires by rubbing sticks together.
Top
Hollywood1
  • Posts:
  • Joined:
    Mon Feb 23, 2015 9:05 am
  • Location:
    Washington

I might be on to something good here! See what you think.
Attachments
lllll.jpg
lllll.jpg (54.64 KiB) Viewed 894 times
Top
Hollywood1
  • Posts:
  • Joined:
    Mon Feb 23, 2015 9:05 am
  • Location:
    Washington

One more pic.
Attachments
unnamedhhhhhhh.jpg
unnamedhhhhhhh.jpg (129.59 KiB) Viewed 894 times
Top
User avatar
  • Posts:
  • Joined:
    Wed Aug 06, 2014 12:48 am
  • Location:
    Melbourne, Australia

Hollywood1, your technique has certainly improved very quickly! Like Jody and most others mention, it takes a lot of Seat Time, but you're certainly on your way.
Trev
EWM Phonenix 355 Pulse MIG set mainly for Aluminum, CIGWeld 300Amp AC/DC TIG, TRANSMIG S3C 300 Amp MIG, etc, etc
Top
Hollywood1
  • Posts:
  • Joined:
    Mon Feb 23, 2015 9:05 am
  • Location:
    Washington

Thanks trackranger. I/m really enjoing welding this aluminum.
Top
haas480
  • Posts:
  • Joined:
    Thu Mar 26, 2015 8:31 am

Hollywood1 wrote:One more picture using step and pause. Thanks Jody, I'm addicted to tig welding.
x2! :D

those welds look good. Hows the penetration, whats the inside of those joints look like?
Here to learn.

Dynasty 200DX
Millermatic 211
GiantTech Cut50D
Top
Hollywood1
  • Posts:
  • Joined:
    Mon Feb 23, 2015 9:05 am
  • Location:
    Washington

Pentetrated to back side slightly.
Top
Hollywood1
  • Posts:
  • Joined:
    Mon Feb 23, 2015 9:05 am
  • Location:
    Washington

Pentetration all the way through could probably turn the heat down a little.
Top
massacre
  • Posts:
  • Joined:
    Sat Feb 28, 2015 10:20 pm
  • Location:
    Massachusetts

I like to weld aluminum too, it's definitely more challenging than steel is. At least to me anyways lol.
Top
'Stang
  • Posts:
  • Joined:
    Sun Aug 03, 2014 11:12 pm
  • Location:
    Rogersville, MO

Hollywood1 wrote:One more picture using step and pause. Thanks Jody, I'm addicted to tig welding.
Nice looking weld. You can learn a lot from Jody's videos. I spent two years in school and learned a lot. Then I started to learn the fine points from Jody! Lol.
Top
Hollywood1
  • Posts:
  • Joined:
    Mon Feb 23, 2015 9:05 am
  • Location:
    Washington

Thank you. This forum has really helped.