Just a note that I am a noobie at tig
I was trying to get some practice in yesterday on some 1/8" aluminum plate and just could not get a puddle and the arc was going everywhere. I checked my settings and all were correct. (125-140 amps on AC with 15 on the flow). I was using 2% thoriated 3/32, with 1/16 filler and a #8 cup. I noticed after several tries and re-checks that my bottle was a little on the low side. Down to about 20 on the gauge. The flow seemed ok...
Will that cause an unstable arc?
Tig welding tips, questions, equipment, applications, instructions, techniques, tig welding machines, troubleshooting tig welding process
jonesk0668
- jonesk0668
-
New Member
-
Posts:
-
Joined:Tue Sep 29, 2015 9:45 pm
-
Location:Southern Indiana
- MosquitoMoto
-
Weldmonger
-
Posts:
-
Joined:Sat Aug 01, 2015 8:38 am
-
Location:The Land Down Under
Hi and welcome.
While I'm not qualified to comment on your gas (although I suspect you are indeed running a bit too low) you'd be better off with 2% Lanthanated or even zirconiated electrodes on aluminium, rather than Thoriated.
Kym
While I'm not qualified to comment on your gas (although I suspect you are indeed running a bit too low) you'd be better off with 2% Lanthanated or even zirconiated electrodes on aluminium, rather than Thoriated.
Kym
- Otto Nobedder
-
Weldmonger
-
Posts:
-
Joined:Thu Jan 06, 2011 11:40 pm
-
Location:Near New Orleans
jonesk0668 wrote:Just a note that I am a noobie at tig
I was trying to get some practice in yesterday on some 1/8" aluminum plate and just could not get a puddle and the arc was going everywhere. I checked my settings and all were correct. (125-140 amps on AC with 15 on the flow). I was using 2% thoriated 3/32, with 1/16 filler and a #8 cup. I noticed after several tries and re-checks that my bottle was a little on the low side. Down to about 20 on the gauge. The flow seemed ok...
Will that cause an unstable arc?
Yes, this can cause issues. If there is any moisture at all in your gas, it will rear it's ugly head when the bottle's nearly done. I assume you've been using the same setup for a bit, in the same way, and the trouble is new? If so, the gas is very likely the culprit.
Welcome to the 'hood (pun intended).
Steve S
If you have a gas issue your tungsten would be dark after it cooled down due to a lack of shielding. But with 140 amps you should have been able to form a puddle no problem even with bum gas and at that amperage the tungsten will grenade with no shielding. Sounds like it could be a grounding problem or a cable connection problem or even a machine problem. Try it on DCEN to see if you get can melt the aluminum. Sometime just switching the polarity switch around a few times can straighten things out if if it's the switch causing the problem.
John
John
Learn 6010 and you will learn to weld
Follow the progress of my students on Twitter @PentaWelding
Follow the progress of my students on Twitter @PentaWelding
Bill Beauregard
- Bill Beauregard
-
Weldmonger
-
Posts:
-
Joined:Thu Jan 24, 2013 9:32 pm
-
Location:Green Mountains of Vermont
People will tell you that only a given tungsten will work. I have a lot of varieties which I use interchangeably on aluminum. Buying new, I try to get lanthanated. I've bought a bunch of old stock thoriated which I use as well. Zapster from the other network uses nothing else. His work shows it works very well. I'd guess you have a gas issue. Something is leaking, or sucking air.
jonesk0668
- jonesk0668
-
New Member
-
Posts:
-
Joined:Tue Sep 29, 2015 9:45 pm
-
Location:Southern Indiana
Thanks for all of your thoughts and advise! I am picking up a new bottle of gas this afternoon and gonna give it a try! I'll keep you posted!
Thanks,
KJ
Thanks,
KJ
Fatjackdurham
- Fatjackdurham
-
New Member
-
Posts:
-
Joined:Fri Sep 25, 2015 4:35 pm
When I took my welding course, we did something with the tungsten to make a sort of round blob on the tip to weld aluminum, but I don't remember exactly what. Can someone remind me what that is? It was like we just ran an arc over the work or some steel and the tungsten melted into a sort of sphere.
Is your tungsten set up that way?
Is your tungsten set up that way?
That sounds like transformer machine practices for pure tungsten.
I'm not an expert on this, but I've seen numerous people here saying that you don't need to do so on an inverter based machine, nor really want to run pure tungsten for aluminum, on an inverter machine.
I'm not an expert on this, but I've seen numerous people here saying that you don't need to do so on an inverter based machine, nor really want to run pure tungsten for aluminum, on an inverter machine.
-Josh
Greasy fingered tinkerer.
Greasy fingered tinkerer.
Well the old dog learned a new trick today. When jones said he could not form a puddle I immediately thought it was a machine problem and gas never entered my mind. In all my days of tig welding I have never seen what he said happened to him, until today. But then again I have never run a cylinder down to nothing or had an extremely low flow rate. I was just running a torch over aluminum forming a puddle and moving around and told a student to slowly turn the gas down and sure enough it happened. The arc went crazy jumping all over the place, very interesting! I was still able to form a puddle but it was all crapped up and at the same time my tungsten was going to heck too and I was never really able to reproduce the crazy arc without the tungsten going bad but I'm sure it could happen under the right conditions. I'm not sure at what flow rate this happened I just know it was below 10 cfh. I was using a standard gas lens and a #7 cup.
John
John
Learn 6010 and you will learn to weld
Follow the progress of my students on Twitter @PentaWelding
Follow the progress of my students on Twitter @PentaWelding
- LtBadd
-
Weldmonger
-
Posts:
-
Joined:Sun Apr 12, 2015 4:00 pm
-
Location:Clearwater FL
-
Contact:
With the transformer machines it was common to "ball" the end of the tungsten by switching to reverse polarity, and at low amps initiate an arc on a clean piece of copper. The current flowing from the work piece would quickly ball the tungsten, thus using only minimal amps determined by the diameter of the tungstenFatjackdurham wrote:When I took my welding course, we did something with the tungsten to make a sort of round blob on the tip to weld aluminum, but I don't remember exactly what. Can someone remind me what that is? It was like we just ran an arc over the work or some steel and the tungsten melted into a sort of sphere.
Is your tungsten set up that way?
Richard
Website
Website
jonesk0668
- jonesk0668
-
New Member
-
Posts:
-
Joined:Tue Sep 29, 2015 9:45 pm
-
Location:Southern Indiana
Ok guys, not much change since last night...
I decided to give you all a look at my machine settings and the results. Don't really know where to go from here?
I decided to give you all a look at my machine settings and the results. Don't really know where to go from here?
- Attachments
-
- 1001151755a.jpg (29.02 KiB) Viewed 1120 times
-
- 1001151755c.jpg (11.65 KiB) Viewed 1120 times
-
- 1001151755b.jpg (30.52 KiB) Viewed 1120 times
-
- 1001151754.jpg (28.29 KiB) Viewed 1120 times
jonesk0668
- jonesk0668
-
New Member
-
Posts:
-
Joined:Tue Sep 29, 2015 9:45 pm
-
Location:Southern Indiana
The gauge you have is a Borden tube style. The scale on it may read 15 cfh but ti can only sense pressure. That is why most people switch over to a floating ball gauge it shows flow.
I have more questions than answers
Josh
Josh
jonesk0668
- jonesk0668
-
New Member
-
Posts:
-
Joined:Tue Sep 29, 2015 9:45 pm
-
Location:Southern Indiana
Switch to or add a floating ball and you will see actually what is flowing. You can also find a floating ball gauge that you just hold over the end of your gas cup to read flow that might be a cheap option.
I have more questions than answers
Josh
Josh
jonesk0668
- jonesk0668
-
New Member
-
Posts:
-
Joined:Tue Sep 29, 2015 9:45 pm
-
Location:Southern Indiana
I found the problem! My hose has cracked and it's leaking gas at connection.
Now just have to buy a new hose...
Now just have to buy a new hose...
- Attachments
-
- 1443744366560686321866.jpg (29.82 KiB) Viewed 1121 times
jonesk0668
- jonesk0668
-
New Member
-
Posts:
-
Joined:Tue Sep 29, 2015 9:45 pm
-
Location:Southern Indiana
Thanks Josh for keeping me on the right track with the gas flow! I knew something was wrong when I changed the gauge and the problem didn't change. I then went to the solenoid and made sure it was working.Poland308 wrote:It's always a relief when you can pin point a problem. At least hose is cheap.
While I was down there, I could hear gas escaping from the connection. Upon further inspection, well, you see what I found.
A new cable/hose is $90 from Lincoln. Not bad.
I'll be sure to post an update when I get the new hose.
Thanks again!
KJ
Bill Beauregard
- Bill Beauregard
-
Weldmonger
-
Posts:
-
Joined:Thu Jan 24, 2013 9:32 pm
-
Location:Green Mountains of Vermont
I believe it was Shovelon who explained it. A transformer based machine producing sine wave will struggle to initiate the EP half of the cycle. The ionization of gas making it electrically conductive is weak. The electrons leaving the workpiece are hampered by less conductive oxides, and contamination. It is late in the beginning of the half cycle that voltage builds to overcome resistance, and begin the arc. This renders the work negative portion of the cycle weaker. For reasons I don't understand pure tungsten was once used for aluminum. Despite the weak nature of return arc, it melted away the point. Might as well make a ball on the end to reduce the erosion. Inverters switch to the other polarity so quickly ionization isn't lost. The work negative half cycle is instant. It moves with the electrons, and corruption, heat. Pure tungsten is not an option with these machines. I would estimate 50/50balance in a transformer machine as similar in cleaning action to an inverter at 80%.
If you have an inverter, give away any pure tungsten. I believe the differences in other varieties are smaller than advertising would suggest. Thoriated has a minute level of radio activity. 2% lanthanated is versatile. others work OK.
If you have an inverter, give away any pure tungsten. I believe the differences in other varieties are smaller than advertising would suggest. Thoriated has a minute level of radio activity. 2% lanthanated is versatile. others work OK.
jonesk0668
- jonesk0668
-
New Member
-
Posts:
-
Joined:Tue Sep 29, 2015 9:45 pm
-
Location:Southern Indiana
UPDATE!
I got my new hose, hooked it up, flipped the switch and struck an arc. All is good in TIG land again!
Thanks for all of the comments and advise!
KJ
I got my new hose, hooked it up, flipped the switch and struck an arc. All is good in TIG land again!
Thanks for all of the comments and advise!
KJ
Return to “Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding”
Jump to
- Introductions & How to Use the Forum
- ↳ Welcome!
- ↳ Member Introductions
- ↳ How to Use the Forum
- ↳ Moderator Applications
- Welding Discussion
- ↳ Metal Cutting
- ↳ Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- ↳ Mig and Flux Core - gas metal arc welding & flux cored arc welding
- ↳ Stick Welding/Arc Welding - Shielded Metal Arc Welding
- ↳ Welding Forum General Shop Talk
- ↳ Welding Certification - Stick/Arc Welding, Tig Welding, Mig Welding Certification tests - Welding Tests of all kinds
- ↳ Welding Projects - Welding project Ideas - Welding project plans
- ↳ Product Reviews
- ↳ Fuel Gas Heating
- Welding Tips & Tricks
- ↳ Video Discussion
- ↳ Wish List
- Announcements & Feedback
- ↳ Forum News
- ↳ Suggestions, Feedback and Support
- Welding Marketplace
- ↳ Welding Jobs - Industrial Welding Jobs - Pipe Welding Jobs - Tig Welding Jobs
- ↳ Classifieds - Buy, Sell, Trade Used Welding Equipment
- Welding Resources
- ↳ Tradeshows, Seminars and Events
- ↳ The Welding Library
- ↳ Education Opportunities