Re: Help me with my Aluminum issue
Posted: Sat Apr 02, 2016 9:28 am
Or set your torch in some type of fixture and watch the display.Poland308 wrote:Video record the display then weld as normal
Page 2 of 2
Re: Help me with my Aluminum issue
Posted: Sat Apr 02, 2016 10:24 am
I might be able to do that later this afternoon when my wife comes home
Sent from my SAMSUNG-SM-G900A using Tapatalk
Sent from my SAMSUNG-SM-G900A using Tapatalk
Re: Help me with my Aluminum issue
Posted: Sat Apr 02, 2016 5:20 pm
Here is the video of me welding some of the same tubing. Believe it or not fixing that slight argon leak solved the problem completely. Thank you everyone for all of your help.
https://youtu.be/8RqoCQ_5Qco
Sent from my SAMSUNG-SM-G900A using Tapatalk
https://youtu.be/8RqoCQ_5Qco
Sent from my SAMSUNG-SM-G900A using Tapatalk
Re: Help me with my Aluminum issue
Posted: Sat Apr 02, 2016 6:59 pm
Sounds good now, gotta like the easy fixDcstang67 wrote:Here is the video of me welding some of the same tubing. Believe it or not fixing that slight argon leak solved the problem completely. Thank you everyone for all of your help.
https://youtu.be/8RqoCQ_5Qco
Sent from my SAMSUNG-SM-G900A using Tapatalk
Re: Help me with my Aluminum issue
Posted: Sat Apr 02, 2016 7:09 pm
I have never heard of a gas leak causing arc instability but hey....
Re: Help me with my Aluminum issue
Posted: Sat Apr 02, 2016 10:15 pm
A small leak under pressure like that can actually suck air in under flow.
Re: Help me with my Aluminum issue
Posted: Sun Apr 03, 2016 5:33 pm
She's welding pretty now!
Sent from my SAMSUNG-SM-G900A using Tapatalk
Sent from my SAMSUNG-SM-G900A using Tapatalk
Re: Help me with my Aluminum issue
Posted: Sun Apr 03, 2016 7:42 pm
Now that your up and running why not consider doing a review of the machine in the "Products Review" forum, seems it's popular and others may benefit from your experience with this unit.Dcstang67 wrote:She's welding pretty now!
Sent from my SAMSUNG-SM-G900A using Tapatalk
Re: Help me with my Aluminum issue
Posted: Tue Apr 05, 2016 12:19 pm
Glad you figured it out. I just had to chase down a small leak on my Dynasty last night as well.
Re: Help me with my Aluminum issue
Posted: Wed Apr 20, 2016 8:57 pm
This same problem drove me crazy on the Dynasty 350 at work for about a week before i figured out the tungsten diameter was set wrong. Glad you figured it out with the gas leak, but if others have this problem check the tungsten diameter setting if your machine has it.
exnailpounder wrote:I thought of something....My machine has a setting for tungsten diameter, I am sure yours does too, did you check that and change it? Also, you referred to arc length as compared to 1/8" metal. That is not arc length, that is stickout and you should have way more than that otherwisw you can't see your puddle. Arc length is when you are welding, how close your electrode is to the puddle. You want to stay within 1/8" or so. Any farther away and your arc will get unstable and wander, among other things. Also, your machine doesn't have enough ass to be doing anything with 1/2" material, especially aluminum. Rule of thumb is 1 amp for every thousand of an inch..example...125 amps for .125 (1/8"). You may have to play with that but that will get you in the ballpark. I would go watch some of Jodys videos. They are great and he doesn't leave anything out.