First Actual Aluminum TIG Job !!!

Posted: Wed Aug 22, 2012 9:05 pm
by rahtreelimbs
A coworker brought me this boat handrail that had a support break off. When I got it it already had a hold piece and a backer already riveted on.

I make no claims to be a great welder but only having been welding aluminum for only a few weeks (teaching myself from Jody's videos) I think I did OK.

The one weld is built up high and wide only because the the gap I had to fill. The opposite side had a gap but I had an easier time doing. All 3 welds were washed over only because I wanted it to look as good as I could make it.


What ya think ???

Image

Image

Image

Image

Image

Re: First Actual Aluminum TIG Job !!!

Posted: Thu Aug 23, 2012 4:32 pm
by rahtreelimbs
Getting an ass chewing on another site about all this. Seems the pinstripe is too close to the weld zone.


I learned something new.


Is it that big a deal ???

Re: First Actual Aluminum TIG Job !!!

Posted: Thu Aug 23, 2012 7:10 pm
by Otto Nobedder
No, the pinstripe is not an issue. Everything looks clean enough.

I think the reason this doesn't look as slick as your "pencil holder" project (nice, BTW) is probably the alloy. This is a marine-grade alloy, and salt water doesn't like some alloys. A little research into marine alloys might lead you to a better filler rod for the purpose, and a slicker looking finished product.

Still, for as little time and practical experience you have in Al, 'At'll work!'

Keep it up!

Steve S.