Posted: Tue Jun 30, 2015 6:58 am
So this ac balance is always an issue , especially to the new ones . So I thought to post this .I have fronius magic wave 2200
in which i try to be good at it . This fronuius is like a wild horse I try to master .This time is my third year and Im close to learn it .
In this machine the cleaning action is -5 to +5 . I assume that i should be using it around -3 something i have not done it
yet . I usually weld old aged aluminum bits who needs the most possible cleaning action so i use +5 when things are a bit better i use +2 yesterday i used 0 . I intend to go less towards EN i will it tried as combination with the proper gas flow .
I use for moment 12 cfh .So the message is this . If you weld for 15 minutes time and the tungsten in not ball up
over the diameter of the tungsten you use you are ok within the proper settings . ( in this case you must stop and regrind the tip of tungsten. )Maybe is not much but for some out there it might be useful ...
in which i try to be good at it . This fronuius is like a wild horse I try to master .This time is my third year and Im close to learn it .
In this machine the cleaning action is -5 to +5 . I assume that i should be using it around -3 something i have not done it
yet . I usually weld old aged aluminum bits who needs the most possible cleaning action so i use +5 when things are a bit better i use +2 yesterday i used 0 . I intend to go less towards EN i will it tried as combination with the proper gas flow .
I use for moment 12 cfh .So the message is this . If you weld for 15 minutes time and the tungsten in not ball up
over the diameter of the tungsten you use you are ok within the proper settings . ( in this case you must stop and regrind the tip of tungsten. )Maybe is not much but for some out there it might be useful ...