I have a classic 300d that I run my control module and then off of that I have my sg spool gun. WELL I am wondering why it did not weld anything like I wanted to. Would burn back the wire all the way to tip and then would hit the metal and just ball and was absolutely crap. Would go up in temp and change wire speed. Was trying everything! Could someone help me please! Maybe the type of wire I was using wasn't right. It's Lincoln's super glaze, but forgot what type. Any help would be great thanks.
Sent from my iPhone using Tapatalk
- Otto Nobedder
-
Weldmonger
-
Posts:
-
Joined:Thu Jan 06, 2011 11:40 pm
-
Location:Near New Orleans
Since this is a spool-gun question, I'll move it to the MIG section. You'll likely get more response there.
Steve S
Steve S
- ShakaWelding
-
Active Member
-
Posts:
-
Joined:Thu Mar 27, 2014 5:36 am
?
Sent from my iPhone using Tapatalk
Sent from my iPhone using Tapatalk
- AKweldshop
-
Weldmonger
-
Posts:
-
Joined:Wed Oct 23, 2013 3:30 pm
-
Location:Palmer AK
Shaka,
Steve moved your post to a better section.
As to your trouble,
Do you have dcep for the current??
Have you tried different wfs?
I like to turn it up till it stubs, than ease it back to a sizzle.
Do you have some pics??
Steve moved your post to a better section.
As to your trouble,
Do you have dcep for the current??
Have you tried different wfs?
I like to turn it up till it stubs, than ease it back to a sizzle.
Do you have some pics??
Just a couple welders and a couple of big hammers and torches.
Men in dirty jeans built this country, while men in clean suits have destroyed it.
Trump/Carson 2016-2024
Men in dirty jeans built this country, while men in clean suits have destroyed it.
Trump/Carson 2016-2024
- ShakaWelding
-
Active Member
-
Posts:
-
Joined:Thu Mar 27, 2014 5:36 am
I'm pretty sure I had it on the right current. I tried different wfs and different temp and everything under the sun it seems like. I am going to use it again shortly and will take pictures.
Sent from my iPad using Tapatalk
Sent from my iPad using Tapatalk
I have the same gun. What is your wire size? Where is your voltage set at? How thick is the base metal? Did you use acetone or wire wheel etc to clean up the aluminum? Did you buy the gun new?
Could ask more questions but let's start there.
Could ask more questions but let's start there.
Be the monkey....
- ShakaWelding
-
Active Member
-
Posts:
-
Joined:Thu Mar 27, 2014 5:36 am
I'm running .035 wire, I tried many different voltages. Base material was 1/8" and I used a stainless steel brush to clean up very well. Gun is not brand new but seems to be in good condition. Also when I have the wire out of the nozzle and touch it to the alum it's starts the arc BUT I didn't even pull the trigger. The trigger does work and feeds the wire through but as soon as I touch it it starts.
I use the module to run the gun and have the module running off my classic 300D
Sent from my iPad using Tapatalk
I use the module to run the gun and have the module running off my classic 300D
Sent from my iPad using Tapatalk
The wire will always be live keep that in mind. I run a very similar setup to yours. You will need to make sure your are switched to 'v on the 300d and electrode positive just like regular mig also make sure you have pure argon. No mix unless its with helium. Your wire speed will have to be close to 80% of full speed (which is around 650ipm on that gun). I always max out the rheostat on the module and just adjust with the dial in the gun handle. Your voltage should be at least 21v. You will have to play with this a bit but start there. Your adjustments should be in small doses as well from there. Feel free to ask more if you need.
Be the monkey....
- ShakaWelding
-
Active Member
-
Posts:
-
Joined:Thu Mar 27, 2014 5:36 am
Switched to v? Not quiet sure of what you mean with that. Everything else I'm going to give a try. Thanks for your help! Really appreciate the help
Sent from my iPad using Tapatalk
Sent from my iPad using Tapatalk
It was supposed to say CV. Sorry. One thing I always do to is my tips are one size bigger than the wire. So with .035 I use a .045 tip. Some say not to do this but I have found it effective. If I run the same size tip the heat makes the already soft aluminum start to rub off and stick inside the tip quickly causing a gummied up mess.
Be the monkey....
- ShakaWelding
-
Active Member
-
Posts:
-
Joined:Thu Mar 27, 2014 5:36 am
On my classic I don't have a cv or cc switch. I will show you some pics of the set up and maybe that will help.
Sent from my iPhone using Tapatalk
- ImageUploadedByTapatalk1401104912.768041.jpg (252.73 KiB) Viewed 1737 times
- ImageUploadedByTapatalk1401104903.285022.jpg (93.09 KiB) Viewed 1737 times
- ImageUploadedByTapatalk1401104892.394248.jpg (90.46 KiB) Viewed 1737 times
Sent from my iPhone using Tapatalk
- ShakaWelding
-
Active Member
-
Posts:
-
Joined:Thu Mar 27, 2014 5:36 am
- ImageUploadedByTapatalk1401104948.505730.jpg (240.87 KiB) Viewed 1736 times
- ImageUploadedByTapatalk1401104937.754475.jpg (112.93 KiB) Viewed 1736 times
Sent from my iPhone using Tapatalk
I have found your problem.... If your 300D doesn't have a CV connection, meaning its a rod burner only (or tig), a spool gun will not work. Module or not it must be on a CV power source. All might is CV and all stick/tig is CC. CV module can be purchased andadded to your machine (I think check with Lincoln) but they must be hard wired into the coils and become a permanent attachment to the welder. Sorry to disappoint you on this one. Double check with your welder repair shop or Lincoln tech support.