I am going to be installing axle sleeves into my dana 30.
The wall thickness of the axle is 1/4" which is the also the thickness of the sleeves.
The plan is to plug-weld three spots on both side of the long tube and once on the short side (front axle).
I will also be welding the end of the tube at the knuckle.
I had planned to use my tig but the material is so oil soaked over the years that is simple not an option (I tried). So I plan to mig weld it. Gave me an excuse to finally buy one, I picked up a Hobart 210 MVP machine.
Are there any specific things I need to be aware of when doing this kind of a plug weld, that would differ from using a tig?
mig and flux core tips and techniques, equipment, filler metal
- weldin mike 27
-
Weldmonger
-
Posts:
-
Joined:Fri Apr 01, 2011 10:59 pm
-
Location:Australia; Victoria
Sorry mate, We only have a few auto type welders here, and they are likely quite busy. On the other hand, we have a large a amount of topics that go unanswered. A quick look at the unanswered posts tab will show you this.
Regards, Mick
Regards, Mick
Firstly, I'm not an auto welder, but I will make comment.
I see the main loads on this repair are the driving force and fatigue stress due to the cyclic nature of operation. To resist these forces, your welds should have plenty of penetration which solid wire mig is notoriously unreliable especially with unclean surfaces and particularly in the hands of the inexperienced.
So for this repair (if you are set on using your new power source) I would recommend using the FCAW (gas shielded) process to ensure good penetration and avoiding cold lap. The better you can clean up the surfaces the better the result will be.
Show us some pics and good luck!
I see the main loads on this repair are the driving force and fatigue stress due to the cyclic nature of operation. To resist these forces, your welds should have plenty of penetration which solid wire mig is notoriously unreliable especially with unclean surfaces and particularly in the hands of the inexperienced.
So for this repair (if you are set on using your new power source) I would recommend using the FCAW (gas shielded) process to ensure good penetration and avoiding cold lap. The better you can clean up the surfaces the better the result will be.
Show us some pics and good luck!
Flat out like a lizard drinkin'
I have Tig welded several cast aluminum (I know this is steel but) small engine cases. They are very porous like your project
I heat and clean with acid then heat and clean till they stop making oily smudge then weld them with the tig. Thats the only way I have been able to get them to weld nice.
I heat and clean with acid then heat and clean till they stop making oily smudge then weld them with the tig. Thats the only way I have been able to get them to weld nice.
My Grandfather Used to say "Grinding a weld to make it pretty doesn't make you a Welder. It makes you a Grinder!"
So finally got it welded in, all the welds were laid down on bright shinny metal.
I think the penetration went well, it was done on both side of the C Gussets.
https://dsm8.smugmug.com/Other/02-Jeep- ... -x89b4Ns/A
https://dsm8.smugmug.com/Other/02-Jeep- ... -ZdNs7fK/A
https://dsm8.smugmug.com/Other/02-Jeep- ... -GXKpNPV/A
I think the penetration went well, it was done on both side of the C Gussets.
https://dsm8.smugmug.com/Other/02-Jeep- ... -x89b4Ns/A
https://dsm8.smugmug.com/Other/02-Jeep- ... -ZdNs7fK/A
https://dsm8.smugmug.com/Other/02-Jeep- ... -GXKpNPV/A
Tie ins look pretty clean. I'm guessing there's a small hole under that dot on the one in the pic. For mig it doesn't look too bad. Every job reveals places that may be adequate, but that we criticize, or over criticize ourselves on.
I have more questions than answers
Josh
Josh
Thanks, there was some gap to be filled in a couple of areas so for those I did a root pass then the cover pass which is what you are seeing in the final pictures.Coldman wrote:Looks good and solid from the outside, no evidence of cold lap. What it's like on the inside, time will tell.
Nice job.
What ever I ended up with is adding strength where there was none before so it is just gravy.
Return to “Mig and Flux Core - gas metal arc welding & flux cored arc welding”
Jump to
- Introductions & How to Use the Forum
- ↳ Welcome!
- ↳ Member Introductions
- ↳ How to Use the Forum
- ↳ Moderator Applications
- Welding Discussion
- ↳ Metal Cutting
- ↳ Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- ↳ Mig and Flux Core - gas metal arc welding & flux cored arc welding
- ↳ Stick Welding/Arc Welding - Shielded Metal Arc Welding
- ↳ Welding Forum General Shop Talk
- ↳ Welding Certification - Stick/Arc Welding, Tig Welding, Mig Welding Certification tests - Welding Tests of all kinds
- ↳ Welding Projects - Welding project Ideas - Welding project plans
- ↳ Product Reviews
- ↳ Fuel Gas Heating
- Welding Tips & Tricks
- ↳ Video Discussion
- ↳ Wish List
- Announcements & Feedback
- ↳ Forum News
- ↳ Suggestions, Feedback and Support
- Welding Marketplace
- ↳ Welding Jobs - Industrial Welding Jobs - Pipe Welding Jobs - Tig Welding Jobs
- ↳ Classifieds - Buy, Sell, Trade Used Welding Equipment
- Welding Resources
- ↳ Tradeshows, Seminars and Events
- ↳ The Welding Library
- ↳ Education Opportunities