looking for some great looking tig art that is also somewhat achievable to replicate as a project to do on some (preferable carbon steel) plate, i realize that i can just google it, but many people don't upload their amazing work to google, so if you got some kickass looking work, i would love if you could share it in this thread :D

here are some examples taken off google to give you some idea of what i meant by tig art
13123.jpg
13123.jpg (122.97 KiB) Viewed 1598 times
b6fe098016cc998c9e2db7ba7816b4bb.jpg
b6fe098016cc998c9e2db7ba7816b4bb.jpg (55.72 KiB) Viewed 1598 times

how do you replicate the scales on the fish? looks like if its at a higher temperature so the puddle is wider, and less frequent dips to replicate the scales farther apart, not sure if that is correct because i'm still a student in welding, but please let me know how the scales where made so i can learn different techniques :)

thank you guys,
regards
noah/Least honorable
Last edited by Least honorable on Sat Apr 23, 2016 12:30 am, edited 1 time in total.
Top
User avatar
  • Posts:
  • Joined:
    Thu Jan 06, 2011 11:40 pm
  • Location:
    Near New Orleans

I stay off of weldporn entirely.

I'm already my own worst critic, I don't need these people reminding me of what I'm not capable of.

You can be a top-notch welder and make a fortune, while never having a weld worthy of the "golden-arm" people on that site.

Steve S
Top
Least honorable
  • Posts:
  • Joined:
    Mon Apr 18, 2016 9:38 pm
  • Location:
    Quebec,Canada

Otto Nobedder wrote:I stay off of weldporn entirely.

I'm already my own worst critic, I don't need these people reminding me of what I'm not capable of.

Steve S

fair enough, im fairly hard on on myself when i weld aswell, but i dont got much experience, still in school, would you happen to know how the fishscales are made? to have that wide shape and damn near perfect scale look?
Top
User avatar
  • Posts:
  • Joined:
    Thu Jan 06, 2011 11:40 pm
  • Location:
    Near New Orleans

I suspect the scales are a manual pulse method, where you move the tungsten to the location of the next "scale", mash the pedal, and add a small dab of filler, then sharply let off so it craters, leaving the space for the next scale. This would create the texture as I see it, but this is only a guess.

Steve S
Top
Poland308
  • Posts:
  • Joined:
    Thu Sep 10, 2015 8:45 pm
  • Location:
    Iowa

Might also try using a fat tungsten with no point to give you a wide arc.
I have more questions than answers

Josh
Top
motox
  • Posts:
  • Joined:
    Thu Nov 28, 2013 12:49 pm
  • Location:
    Delaware

thats a lot of rod and argon
craig
htp invertig 221
syncrowave 250
miller 140 mig
hypertherm plasma
morse 14 metal devil
Top
soutthpaw
  • Posts:
  • Joined:
    Thu Sep 18, 2014 12:14 pm
  • Location:
    Sparks, NV

Large filler rod would be my guess
Reason being, especially with aluminum, if you use large rod, it will cool the puddle very rapidly and freeze before the puddle has time to wet out. Combined with a slow pulse or manual pulse might get that look. A steady hand is the other part you need...
Image
Top
Least honorable
  • Posts:
  • Joined:
    Mon Apr 18, 2016 9:38 pm
  • Location:
    Quebec,Canada

soutthpaw wrote:Large filler rod would be my guess
Reason being, especially with aluminum
You think it's aluminum? Does the type matter much? I thought the baseplate looked a lil like some carbon steel, but you're probably right.

[Edit] now that I look closer, I realize the cleaning action all around the welds
Top
exnailpounder
  • Posts:
  • Joined:
    Thu Dec 25, 2014 9:25 am
  • Location:
    near Chicago

The bottom pic is Mig or stick welded (take a good look). I don't think the fish was all bead stacked. I think the weldor put together some sore of base to stack beads on. It would take forever to stack all those beads and cost a fortune for rod and argon if it was all bead stacked. Plus the metal would be a couple inches thick. Maybe if you had a 1000 amp welder :lol:
Last edited by exnailpounder on Tue Apr 26, 2016 4:35 pm, edited 1 time in total.
Ifyoucantellmewhatthissaysiwillbuyyouabeer.
Top
soutthpaw
  • Posts:
  • Joined:
    Thu Sep 18, 2014 12:14 pm
  • Location:
    Sparks, NV

Might be a good welder, but does not know much about fish. All the scales are stacked in the wrong direction!

Sent from mobile. Not responsible for Typos
Top
exnailpounder
  • Posts:
  • Joined:
    Thu Dec 25, 2014 9:25 am
  • Location:
    near Chicago

soutthpaw wrote:Might be a good welder, but does not know much about fish. All the scales are stacked in the wrong direction!

Sent from mobile. Not responsible for Typos
Good eye!
Ifyoucantellmewhatthissaysiwillbuyyouabeer.
Top
User avatar
  • Posts:
  • Joined:
    Sun Sep 22, 2013 10:14 am
  • Location:
    Minneapolis Mn 55407

maybe it swims tail first? New species!
Everlast 250EX
Miller 250 syncrowave
Sharp LMV Vertical Mill
Takisawa TSL-800-D Lathe
Coupla Bandsaws,Grinders,surface grinder,tool/cutter grinder
and more stuff than I deserve(Thanks Significant Other)
Top
Post Reply

Return to “Welding Projects - Welding project Ideas - Welding project plans”